A physically-based dislocation theory of plasticity is derived within an extended continuum
mechanical context. Thermodynamically consistent flow rules at the grain boundaries are
derived. With an analytical solution of a three-phase periodic laminate dislocation pile-up at
grain boundaries and dislocation transmission through the grain boundaries are investigated.
For the finite element implementations numerically efficient approaches are introduced based
on accumulated field variables.